ZHEJIANG TOP BEARINGS CO., LTD.
YOUR TOP PARTERNER FOR PLAIN BEARINGS and ROLLING BEARINGS.
Add to Cart
ZrO2 Ceramic Bearings , Full Ceramic Bearings
ZrO2 Full ceramic bearing have excellence performance as special electrical and magnetism resistance, wear and corrosion resistance, lubrication and maintenance free when working, especially high and low-temperature application etc., could be used in awful environment and specially condition. The rings and balls were made by full ceramic material:ZrO2, as a standard construction, the cage was made by PTFE, generally we also could make the cage with GFRPA66-25, PEEK, PI, AISI SUS304, SUS316, Cu, etc.
| Comparison of bearing material technical data | ||||||
| Technical data | unit | GCr15 | 9Cr18 | Si3N4 | AL203 | ZrO2 |
| Density | g/cm³ | 7.8 | 7.9 | 3.2 | 3.95 | 6 |
| a Coefficient of expansion | 10^-6/℃ | 11 | 17 | 3.2 | 9.1 | 10.5 |
| E modulus of elasticity | Gpa | 208 | 200 | 320 | 380 | 210 |
| μ Poisson ratio | 0.3 | 0.3 | 0.26 | 0.27 | 0.3 | |
| HV Hardness | 800 | 700 | 1700 | 1800 | 1300 | |
| δ Flexural strength | Mpa | 2400 | 2600 | 900 | 220 | 1000 |
| δ Compressive Strength | MPa | 2000 | 1500 | 3500 | ||
| Kc Impact strength | Nm/cm² | 20 | 25 | 7 | 3.5 | 11 |
| λ Thermal conductivity | W/mk | 30-40 | 15 | 3.5 | 25 | 2.5 |
| Ω Specific resistivity | mm²/m | 1 | 0.75 | 10^18 | 10^8 | 10^5 |
| Specific heat | J/KgK | 450 | 450 | 800 | 880 | 400 |
| Application temperature | ℃ | 120 | 150 | 1000 | 1850 | 800 |
| Anti-corrossion | No | poor | Good | Good | Good | |
| Cycle stress | 10*10^6 | 10*10^6 | 50*10^6 | 30*10^6 | 50*10^6 | |
| Destroy model | peel | peel | peel | fracture | peel/fracture | |
| Anti-magnetism | Yes | Yes | No | No | No | |
| Dimension stability | bad | poor | Good | Good | Good | |
| Insulate properties | No insulation | No insulation | Good | Good | Good | |
| Basic properties of staple engineer plastic | ||||||||
| Material | HDPE | PP | POM | PA66 | PVDF | PPS | PTFE | PEEK |
| Long-time working temp. | 90 | 100 | 110 | 100 | 150 | 230 | 260 | 280 |
| Density | g/cm3 | 0.91 | 1.42 | 1.14 | 1.77 | 1.35 | 2.18 | 1.32 |
| Ball indentation hardness | 50 | 80 | 170 | 170 | 80 | 190 | 30 | |
| Tensile stress | 25 | 30 | 70 | 80 | 50 | 75 | 25 | 95 |
| Sliding friction coefficient | 0.29 | 0.3 | 0.34 | 0.35-0.42 | 0.3 | 0.08-0.1 | 0.3-0.38 | |
| Melted temperature | 130 | 165 | 175 | 260 | 172 | 280 | 327 | 343 |
| Short-time highest application temperature | 90 | 140 | 150 | 170 | 150 | 260 | 260 | 300 |
| Coet of Inear expansion (10^-5/K) | 13-15 | 17 | 10 | 8 | 13 | 5 | 12 | 5 |
| Dielectric constant at 1 Mhz(10^6HZ) | 2.4 | 2.25 | 3.7 | 3.6-5 | 8 | 2.1 | 3.2-3.3 | |
| Volume resisrivity (Ω·cm) | >10^15 | >10^24 | >10^14 | 10^13 | 10^12 | >10^13 | 10^14 | 10^13 |
| flammability UL94 | + | + | - | (+) | (+) | - | + | + |
| Anti-weathering | - | - | - | - | - | - | + | - |
| Note: + =resistant; (+) =partly resistant; - =non-resistant | ||||||||